Zirconia Ceramic Grinding Media Ball

Ce-TZP Zirconia ceramic grinding media ball is a high-density milling media that maximizes grinding efficiency. Its superior quality ensures high performance and cost-effective results. This grade is an affordable solution recommended for large volume mills, either vertical or horizontal.

Product Details

Product Introduction:

Ce-TZP Zirconia ceramic grinding media ball is a high-density milling media that maximizes grinding efficiency. Its superior quality ensures high performance and cost-effective results. This grade is an affordable solution recommended for large volume mills, either vertical or horizontal.

Specification:

Item	Unit	Specification
Composition	wt%	85-88% ZrO₂ 10-14% CeO₂
Bulk Density	Kg/L	>3.75 (Φ2mm)
Specific Density	g/cm³	≥6.2
Hardness	Moh's	>8.5
Elastic modulus	GPa	200
Thermal Conductivity	W/m.K	3
Crushing Load	KN	≥20 (Φ2mm)
Fracture Toughness	MPam1-2	9
Grain size	µm	≤0.5
Wear loss	ppm/h	<0.15
Color		Black gray

Sizes Φ:

Size (mm)	Size (mm)	Size (mm)	Size (mm)	Size (mm)
0.4-0.5	0.6-0.8	0.9-1.0	1.4-1.6	2.2-2.5
0.4-0.6	0.7-0.8	0.9-1.1	1.6-1.8	2.5-2.8
0.5-0.7	0.7-0.9	1.0-1.2	1.8-2.0	2.8-3.2
0.6-0.7	0.8-1.0	1.2-1.4	2.0-2.2	3.2-3.5

Avantages:

1.	Ce-TZP Zirconia ceramic grinding media ball combines high density and hardness to ensure the highest milling efficiency.
2.	The extreme low level of wear during milling prevents any contamination of the final product, which makes Kingda Ce-TZP Zirconia beads the perfect solution for white mineral applications.
3.	High mechanical strength, impact resistance, high speed operation without fragmentation.

Applications:

1. It is suitable for mineral pigments and fillers like TiO₂, CaCO₃, talc, clay, barites or zeolites.

2. High strength, high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics.

Production Details: