1) Weigh each raw material with a total weight of 200kg according to the ratio, put it into a ceramic grinding ball mill, then add 133kg distilled water and 2.4kg ammonium polyacrylate to the ceramic grinding ball mill, wet grind for 20h, and use a laser particle size analyzer to measure the slurry particle size as After the median diameter size is 0.3-0.6μm, stop grinding and unloading, use a centrifugal spray-drying tower to spray dry powder, and then spray dry powder through vibration screening to take 180-200 mesh spray powder as seeds;
2) Step 1) The dry powder after sieving is crushed twice with a pin-type crusher, and the powder is obtained after removing iron through a 200 mesh sieve and an electromagnetic iron remover; add the step 1) to the rolling ball machine Seeds, after spraying water, add powder to make the powder wrap the seeds, roll long balls, and grow into balls with a size of 2-3mm to get green balls;
3) The green ball of step 2) is polished at room temperature and dried for 3h and 30h to reduce the moisture to 0.5%, and then burned in a roller kiln at 1360℃ for 2h to obtain high-performance ceramic grinding balls.