0.4mm zirconia milling balls

* Color: Opaque white
* Maximum Temperature:3075° F, except balls are 2000° F
* Machine: Use diamond grinding wheel
* Porosity: Nonporous
* Compressive Strength:300,000 psi

Product Details

Zirconium oxide zirconia zro2 ceramic beads/balls

Product Introduction:

0.4mm zirconia milling balls Kingda Y-TZP consists of yttrium stabilized zirconium oxide. Yttrium Stabilized Zirconia (Y-TZP) is the strongest ceramic material we offer. Y-TZP is a purely tetragonal phase, fine grain material.

Chemical Composition:

Composition	ZrO₂	Y₂O₃	Other
Content %	94.8±0.2	5.1±0.1	0.1%

Physical Properties:

Specific Gravity g/cm³	Bulk Density g/cm³	Hardness Hv	Fracture Toughness MPam^1-2	Crushing Load KN (Φ2.0mm)	Grain size um	Wear loss (%)	Sphericity (%)
≥6.02	≥ 3.70	≥1250	9	≥20	≤0.5	≤0.08	≥98

Ball Sizes:

Size (mm)	Size (mm)	Size (mm)	Size (mm)	Size (mm)
Φ0.08-0.12	Φ0.12-0.18	Φ0.18-0.22	Φ0.22-0.28	Φ0.28-0.35
Φ0.3-0.4	Φ0.4-0.6	Φ0.6-0.8	Φ0.8-1.0	Φ1.0-1.2
Φ1.2-1.4	Φ1.4-1.6	Φ1.6-1.8	Φ1.8-2.0	2.0-2.2
Φ2.2-2.4	Φ2.4-2.6	Φ2.6-2.8	Φ2.8-3.0	Φ3.0-3.2
Φ3.2-3.5	Φ4	Φ5	Φ6	Φ7
Φ8	Φ10	Φ12	Φ15	Φ17
Φ20	Φ25	Φ30	Φ40	Φ50

Applications:

0.4mm zirconia milling balls is widely used for grinding, dispersing and polishing as following: inkjets inks, electronic slurries, raw material of battery, screen printing inks, coating, painting, pigment, ceramic and cosmetic, jewelry and other nanoparticles products.

Production Details: